Nonisothermal crystallization behavior of exfoliated poly(ethylene terephthalate)‐layered silicate nanocomposites in the presence and absence of organic modifier

Exfoliated poly(ethylene terephthalate) (PET)‐layered silicate nanocomposites (P_etLSNs) excluding (P_etLSN_eom) and including (P_etLSN_iom) organic modifiers were obtained by solution methods with and without solvent‐nonsolvent system, respectively. From wide angle X‐ray diffraction and high resolution transmission electron microscopy, both P_etLSNs were found to have exfoliated structure attributed to sufficient dispersion of silicate in prepared solvents, regardless of sample preparation method. However, organic modifier in P_etLSN_eom was confirmed to be well removed by elemental analysis, whereas organic modifier was still remained in P_etLSN_iom. Thus, the effect of the presence and absence of organic modifiers in P_etLSNs on the nonisothermal crystallization behavior was investigated by differential scanning calorimetry (DSC) on the basis of a modified Avrami analysis and polarized optical microscopy (POM). From DSC results, it was found that both P_etLSNs had higher degrees of crystallinity and shorter crystallization half‐times than neat PET, because of the dispersed silicate layers acted as nucleating agents in both P_etLSNs. However, P_etLSN_iom exhibited a lower degree of crystallinity and longer half‐time of crystallization than P_etLSN_eom. Difference of crystallization behavior between P_etLSN_eom and P_etLSN_iom was ascribed to organic modifier in P_etLSN_iom, which may act as crystallization inhibitors. POM measurements also revealed the results which were in good agreement with crystallization behavior observed from DSC measurement. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 989–999, 2008