Synthesis and characterization of fluorene‐based low‐band gap copolymers containing propylenedioxythiophene and benzothiadiazole derivatives for bulk heterojunction photovoltaic cell applications

The following noble series of soluble π‐conjugated statistical copolymers was synthesized by palladium catalyzed Suzuki polymerization: poly(9,9‐dioctylfluorene)‐alt‐(4,7‐bis(3′,3′‐dihepyl‐3,4‐propylenedioxythienyl)‐2,1,3‐benzothiadiazole)] (PFO‐PTBT) derived from poly(9,9‐dioctylfluorene) (PFO) and poly(4,7‐bis(3′,3′‐dihepyl‐3,4‐propylenedioxythienyl)‐2,1,3‐benzothiadiazole)] poly(heptyl₄‐PTBT). The structure and properties of these polymers were characterized using ¹H‐, ¹³C‐NMR, UV–visible spectroscopy, elemental analysis, GPC, DSC, TGA, photoluminescence (PL), and cyclic voltammetry (CV). The statistical copolymers, PFO‐PTBT (9:1, 8.4:1.6, 6.5:3.5), were soluble in common organic solvents and easily spin coated onto indium‐tin oxide (ITO) coated glass substrates. The weight‐average molecular weight (M_w) and polydispersity of the PFO‐PTBT ranged from (1.0–4.2) × 10⁴ and 1.5–2.3, respectively. Bulk heterojunction photovoltaic cells with an ITO/PEDOT/PFO‐PTBT:PCBM/LiF/Al configuration were fabricated, and the devices using PFOPTBT (6.5:3.5) showed the best performance compared with those using PFO‐PTBT (9:1, 8.4:1.6). A maximum power conversion efficiency (PCE) of 0.50% (V_oc = 0.66 V, FF = 0.29) was achieved with PFO‐PTBT (6.5:3.5). © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 6175–6184, 2008