The effect of structure on the thermoresponsive nature of well‐defined poly(oligo(ethylene oxide) methacrylates) synthesized by ATRP |
| |
Authors: | Shin‐Ichi Yamamoto Joanna Pietrasik Krzysztof Matyjaszewski |
| |
Institution: | Center for Macromolecular Engineering, Department of Chemistry, Carnegie Mellon University, 4400 Fifth Avenue, Pittsburgh, Pennsylvania 15213 |
| |
Abstract: | Statistical copolymers of di(ethylene glycol) methyl ether methacrylate (MEO2MA) and tri(ethylene glycol) methyl ether methacrylate (MEO3MA) were synthesized by atom transfer radical polymerization (ATRP) providing copolymers with controlled composition and molecular weights ranging from Mn = 8,300–56,500 with polydispersity indexes (Mw/Mn) between 1.19 and 1.28. The lower critical solution temperature (LCST) of the copolymers increased with the mole fraction of MEO3MA in the copolymer over the range from 26 to 52 °C. The average hydrodynamic diameter, measured by dynamic light scattering, varied with temperature above the LCST. These two monomers were also block copolymerized by ATRP to form polymers with molecular weight of Mn = 30,000 and Mw/Mn from 1.12 to 1.21. The LCST of the block copolymers shifted toward the LCST of the major segment, as compared to the value measured for the statistical copolymers at the same composition. As temperature increased, micelles, consisting of aggregated PMEO2MA cores and PMEO3MA shell, were formed. The micelles aggregated upon further heating to precipitate as larger particles. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 194–202, 2008 |
| |
Keywords: | atom transfer radical polymerization (ATRP) block copolymers living radical polymerization (LRP) micelles stimuli‐sensitive polymers water‐soluble polymer |
|
|