Studies on long lasting optical properties of Eu2+ and Dy3+ doped di-barium magnesium silicate phosphors

Di-bariummagnesium silicate phosphors doped with europiumand dysprosium were prepared under a weak reducing atmosphere. X-ray diffraction pattern of the sample was also done that confirmed the proper preparation of the phosphor. Scanning electron microscope (SEM) images confirmed that the sample has regular surface and uniform grain size distribution. Comparative studies of phosphorescence decay of Ba₂MgSi₂O₇:Eu²⁺, Dy³⁺ phosphors with different concentration of Dy³⁺ were done. The phosphor with 0.5/1.5 mol% of Eu/Dy, exhibited optimum green color afterglow properties. This emission is expected to arise due to transition of Eu²⁺ ions from any of the sublevels of 4f⁶5d¹ configuration to ⁸S_7/2 level of the 4f⁷ configuration. For a suitable trap depth, the trap concentration is expected to be proportional to the concentration of Dy³⁺. These traps are responsible for holding the charge career for a reasonable time, subsequently for increasing the time of afterglow. Hence, optimum Dy³⁺ concentration produces the longer afterglow duration with higher intensity of luminescence signals. Trap depth were also calculated using thermoluminescence glow curve which was indicative of formation of traps suitable for long afterglow.