Effect of the Conformation of Polymer Chain on the Reduction Rate of Polyacrylatopentaamminecobalt(III) by Polymer-Bound Ferrous Chelates and the Excited State of Tris(Bipyridine)Ruthenium(Ii)

Electron transfer reactions of Co(NH₃)₅PAA (PAA = polyacrylic acid) with either the polyanionic polymer-bound ferrous chelate, Fe¹¹P-SS (P-SS = vinylbenzylaminediacetate-co-styrenesulfonate) or the uncharged polymer-bound ferrous chelate, Fe¹¹P-VPRo (P-VPRo = vinylbenzylaminediacetate-co-vinylpyrrolidone), and the Ru(bpy)²⁺ ₃ photosensitized reduction of Co(NH₃)₅PAA have been investigated in aqueous solutions at pH 5.4, I = 0.06 (I is ionic strength), and 25°C. For the ferrous chelate reductions, the second-order rate constants for Fe¹¹-PSS and Fe¹¹P-VPRo were almost equal to that for the corresponding nonpolymer-bound ferrous chelate, Fe¹¹BDA (BDA = benzylaminediacetate). The results indicate that there is no appreciable steric hindrance due to the polymer chains of the polymer-bound ferrous chelates and that the effect of columbic repulsion force between the polyanion chains can be ignored for the reaction of Co(NH₃)₅PAA with Fe¹¹P-SS. The results also suggest that there are two kinds of the pendant Co(III) species, “reactive” and “inert.” The inert Co(III) species are shielded by the polymer chains from attack of the Fe(II) chelates that are present in the bulk solutions. A similar reaction behavior was observed in the Ru(bpy)²⁺ ₃ photosensitized reduction of Co(NH₃)₅PAA at pH 5.4. For the Co(III) complex having an extremely few Co(III) complex moieties on the polymer chain, almost all of the Co(III) groups were hardly reduced by the excited state of Ru(bpy)²⁺ ₃, and reverse quenching occurred due to binding of the Ru(bpy)²⁺ ₃ to the polyacrylic acid chain of the polymer complex. On the other hand, for Co(NH₃)₅PAA with a relatively large number of the Co(III) moieties on the polymer chain, lifetime measurements at a higher concentration of the Ru(bpy)²⁺ ₃ showed a double-exponential fit, which suggests that there are two parallel decay processes. The fast and slow components mainly correspond to the decays: Ru(bpy)²⁺ ₃ quenched by Co(III) and reverse quenching due to binding of Ru(bpy)²⁺ ₃ into the compact polymer chains.