On the sub-Tg annealing of uniaxially oriented and unoriented atactic polystyrene |
| |
Authors: | C Carfagna L Nicodemo L Nicolais |
| |
Institution: | (1) Dipartimento di Chimica, Universitá di Napoli, Napoli, Italy;(2) Dipartimento di Ingegneria dei Materiali e della Produzione, Universitá di Napoli, Napoli, Italy |
| |
Abstract: | DSC analysis was performed on uniaxially oriented and unoriented atactic polystyrene samples prior to and after annealing at 80 °C. With increasing annealing times, an endothermic peak appeared, whose area increased with the duration of the annealing period. No difference was found between the endotherm areas for the oriented and the unoriented polymer.The DSC curve of the unannealed oriented polystyrene exhibited a relaxation exotherm. DSC and relaxation studies indicated that this relaxation exotherm was independent of the main chain orientation; it may rather be due to sample densification.
Zusammenfassung Uniaxial orientierte und unorientierte ataktische Polystyrenproben wurden vor und nach dem Tempern bei 80° mittels DSC untersucht. Mit länger werdender Temperungszeit erscheint in endothermer Peak, dessen Fläche mit der Dauer der Temperungsperiode ansteigt. Die Flächen der endothermen Peaks von orientierten und unorientierten Polymeren unterscheiden sich nicht. Die DSC-Kurve von ungetempertem orientiertem Polystyren zeigt einen exothermen Relaxationseffekt. DSC und Relaxationsuntersuchungen ergaben, daß dieser exotherme Relaxationseffekt unabhängig von der Orientierung der Hauptkette ist und eher einer Probeverdichtung zuzuschreiben ist.
80°. , . . , , . , , .
We are grateful to Prof. B. Wunderlich of the Rensselaer Polytechnic Institute, New York, for useful discussions. The financial support of C.N.R. (progetto finalizzato chimica fine e secondaria) is gratefully acknowledged. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|