Size-controlled synthesis of LaAlO3 by reverse micelle method: Investigation of the effect of water-to-surfactant ratio on the particle size

Lanthanum monoaluminate (LaAlO₃) nanoparticles have been synthesized using microreactors made of poly(oxyethylene) nonylphenyl ether (Igepal CO-520)/water/cyclohexane microemulsions. The control of particle size was achieved by varying the water-to-surfactant molar ratio. The synthesized and calcined powders were characterized by thermogravimetry–differential thermal analysis (TGA-DTA), X-ray diffraction analysis (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and Fourier transform infrared spectroscopy (FTIR). Differential thermal analysis showed that LaAlO₃ phase transformation decreases with increase in water/surfactant (R) value. Pure LaAlO₃ phase was synthesized by annealing at 800 °C for 2 h in air directly from amorphous precursors, without formation of intermediate phase. The average particle size was found to increase with increase in water-to-surfactant ratio (R). FTIR analysis was carried to monitor the elimination of residual oil and surfactant phases from the microemulsion-derived precursor and calcined powder.