Low-temperature RPCVD of Si,SiGe alloy,and Si1−yCy films on Si substrates using trisilane (Silcore)

Si homo-epitaxial growth by low-temperature reduced pressure chemical vapor deposition (RPCVD) using trisilane (Si₃H₈) has been investigated. The CVD growth of Si films from trisilane and silane on Si substrates are compared at temperatures between 500 and 950 °C. It is demonstrated that trisilane efficiency increases versus silane's one as the surface temperature decreases. Si epilayers from trisilane, with low surface roughness, are achieved at 600 and 550 °C with a growth rate equal to 12.4 and 4.3 nm min⁻¹, respectively. It is also shown that Si_1−xGe_x layers can be deposited using trisilane chemistry.