Texture of molybdenum thin films on SrTiO3(1 0 0): A RHEED study

The structure of ultrathin Mo films on SrTiO₃(1 0 0) was studied by in situ reflection high-energy electron diffraction (RHEED). A different structure was observed for films less than 20 Å thick than for thicker films. These films were epitaxial and had a metastable structure. Thicker films had the dimensions of equilibrium bcc Mo(1 1 0). Relaxation processes transformed the metastable Mo into bcc Mo, resulting in the following orientation relationships between Mo and SrTiO₃: (1 1 0)[0 0 1]_bcc Mo ∥ (1 0 0)[0 0 1]_SrTiO3 and (1 1 0)[1 1 1]_bcc Mo ∥ (1 0 0)[0 1 1]_SrTiO3. The formation of such specific orientations is related to transformations via the Bain and Needle Path, respectively.