Reproducible tritium generation in electrochemical cells employing palladium cathodes with high deuterium loading

Reproducible tritium generation well above background has been observed in tightly closed D₂SO₄-containing cells in four out of four Pd wire cathodes of one type. Tritium analysis was performed before and after each experiment on the Pd, the electrolyte and the gas in the head space. No tritium generation was observed in four identical Pd cathodes in H₂SO₄ cells operated at the same time under the same conditions. A cyclic loading-unloading regime with low current densities, rather than the usual continuous constant current regime, was employed to attain D/Pd and H/Pd loadings of 1±0.05 reproducibly. D/Pd loadings greater than 0.8±0.05 appear to be necessary to generate tritium. The largest amount of tritium, generated in 7 days of continuous electrolysis, was 2.1 × 10¹¹ tritium atoms, compared with a background of 4 × 10⁹ tritium atoms. The concentration of tritium and its axial distribution in the Pd were determined and concentrations of up to 9 × 10¹⁰ atoms/g Pd were found compared with a maximum background of 5 × 10⁸ atoms g⁻¹. The T/D ratio in the Pd is about 100 times larger than in the electrolyte or gas and indicates that tritium generation occurs in the Pd interior rather than at its surface. No tritium generation was observed in two other types of Pd electrodes in D₂SO₄, despite the attainment of D/Pd ratios near 1:1. Thus high D/Pd ratios appear to be a necessary but not sufficient condition for tritium generation in D₂SO₄ electrolysis.