Effect of temperature on the fracture surfaces of filled systems based on SKS-85 butadiene-styrene copolymer

The tear fracture surfaces of mixtures of SKS-85 butadiene — styrene copolymer (85% styrene) with ordinary (carbon black, chalk) and polymeric (Kapron and cellophane powder) fillers have been investigated on the interval from –60 to +40°C. As the temperature varies within the limits of the glassy state (T_g SKS-85=+24°C) of the filled polymer, the nature of the fracture surface of specimens of filled mixtures, like that of the unfilled polymer, changes; in the region of the temperature transition of the copolymer associated with the mobility of the phenyl groups (–10±5°C) there is a slowing of the fracture process. At temperatures below the T_g of the copolymer the tear fracture surfaces of specimens of mixtures containing ordinary and polymeric fillers differ sharply. The introduction of fillers (20 vol. %) with a coefficient of thermal expansion different from that of the filled polymer considerably reduces the resistance of the material to fracture and leads to a sharp increase in the rate of crack propagation; the introduction of polymeric fillers with coefficients of thermal expansion similar to that of the filled polymer leads to an increase in the resistance of the material to fracture and to a decrease in the rate of crack propagation.Moscow Technological Institute of the Meat and Dairy Industry; State Institute of Polymer Adhesives, Kirovakan. Translated from Mekhanika Polimerov, No. 5, pp. 819–826, September–October, 1969.