A new selenocyanate-selective electrode based on an Urushi matrix-membrane

Summary A selenocyanate-selective electrode was prepared from tri-n-octylmethylammonium selenocyanate ion-exchanger and a matrix, Urushi. A linear potential-concentration curve was obtained within the concentration range of 10^–1–10^–5 mol/l selenocyanate. When 45–50 wt% of trin-octylmethylammonium selenocyanate ion-exchanger and 55-50 wt% of raw Urushi latex were used, the slope of the linear part of the potential-concentration curve was 60 mV per decade change of the selenocyanate concentration. The static response time was less than 30 s. The electrode exhibited constant potential within the pH range 2–10. The selectivity coefficient for the electrode was measured with the mixed solution method. The electrode was used for the measurement of the formation of selenocyanate from selenious acid, ascorbic acid and potassium cyanide.

---

Neue Selenocyanat-selektive Elektrode mit Urushi-Matrixmembran

Zusammenfassung Eine Selenocyanat-selective Elektrode wurde aus einem Tri-n-octylmethylammonium-Selenocyanat-Austauscher und einer Urushi-Matrix hergestellt. Lineare Potential-Konzentrations-Kurven wurden im Konzentrationsbereich 10^–1 bis 10^–5 mol/l Selenocyanat erhalten. Bei Einsatz von 45–50% Tri-n-octylmethylammonium-Selenocyanat und 55-50% rohem Urushi-Latex betrug die Neigung des linearen Teils der Potential-Konzentrationskurve 60 mV pro Zehnerpotenz Selenocyanatkonzentration. Die statische Ansprechzeit war weniger als 30 s. Die Elektrode wies im pH-Bereich von 2–10 ein konstantes Potential auf. Der Selektivitätskoeffizent wurde nach der Methode der Lösungsgemische gemessen. Die Elektrode wurde angewendet zur Messung der Bildung von Selenocyanat aus seleniger Säure, Ascorbinsäure und Kaliumcyanid.