Structural and thermochemical chemisorption of CO2 on Li(4+x)(Si(1-x)Al(x))O4 and Li(4-x)(Si(1-x)V(x))O4 solid solutions

Different Li(4)SiO(4) solid solutions containing aluminum (Li(4+x)(Si(1-x)Al(x))O(4)) or vanadium (Li(4-x)(Si(1-x)V(x))O(4)) were prepared by solid state reactions. Samples were characterized by X-ray diffraction and solid state nuclear magnetic resonance. Then, samples were tested as CO(2) captors. Characterization results show that both, aluminum and vanadium ions, occupy silicon sites into the Li(4)SiO(4) lattice. Thus, the dissolution of aluminum is compensated by Li(1+) interstitials, while the dissolution of vanadium leads to lithium vacancies formation. Finally, the CO(2) capture evaluation shows that the aluminum presence into the Li(4)SiO(4) structure highly improves the CO(2) chemisorption, and on the contrary, vanadium addition inhibits it. The differences observed between the CO(2) chemisorption processes are mainly correlated to the different lithium secondary phases produced in each case and their corresponding diffusion properties.