| Bi2Ti2O7薄膜的自组装法制备及表征 |
| |
| 引用本文： | 夏傲,黄剑锋,谈国强,尹君. Bi2Ti2O7薄膜的自组装法制备及表征[J]. 无机化学学报, 2013, 29(18) |
| |
| 作者姓名： | 夏傲 黄剑锋 谈国强 尹君 |
| |
| 作者单位： | 陕西科技大学教育部轻化工助剂化学与技术重点实验室, 西安 710021;陕西科技大学教育部轻化工助剂化学与技术重点实验室, 西安 710021;陕西科技大学教育部轻化工助剂化学与技术重点实验室, 西安 710021;陕西科技大学教育部轻化工助剂化学与技术重点实验室, 西安 710021 |
| |
| 基金项目： | 国家青年科学基金(No.51002092);陕西省自然科学基金(No.2010JM6013)资助项目。 |
| |
| 摘 要： | 以Bi(NO3)3·5H2O和Ti(OC4H9)4为原料,采用自组装单层膜技术,在负载有功能化三氯十八烷基硅烷(octadecyl-trichloro-silane,OTS)的FTO基板上制备了Bi2Ti2O7 薄膜。基板表面的亲水性测试表明,紫外照射使OTS自组装单层膜表面由疏水转变为亲水,实现功能化。借助X射线衍射(XRD)、X射线能量色散谱(EDS)、扫描电子显微镜(SEM)和原子力显微镜(AFM)分析分别对Bi2Ti2O7薄膜的组成、结构和微观形貌进行了表征。结果表明,沉积溶液浓度为0.02 mol·L-1时,所得Bi2Ti2O7薄膜均匀致密。560 ℃热处理1 h、厚度为0.4 μm的Bi2Ti2O7薄膜在100 kHz的介电常数为153,介电损耗为0.089。
|
| 关 键 词： | Bi2Ti2O7 薄膜 自组装单层膜 介电性能 |
Preparation and Characterization of Bi2Ti2O7 Thin Films from Self-Assembled Monolayer Technique |
| |
| XIA Ao,HUANG Jian-Feng,TAN Guo-Qiang and YIN Jun. Preparation and Characterization of Bi2Ti2O7 Thin Films from Self-Assembled Monolayer Technique[J]. Chinese Journal of Inorganic Chemistry, 2013, 29(18) |
| |
| Authors: | XIA Ao HUANG Jian-Feng TAN Guo-Qiang YIN Jun |
| |
| Affiliation: | Key Laboratory of Auxiliary Chemistry and Technology for Chemical Industry, Ministry of Education of China, Shaanxi University of Science and Technology, Weiyang District, Xi'an 710021, China;Key Laboratory of Auxiliary Chemistry and Technology for Chemical Industry, Ministry of Education of China, Shaanxi University of Science and Technology, Weiyang District, Xi'an 710021, China;Key Laboratory of Auxiliary Chemistry and Technology for Chemical Industry, Ministry of Education of China, Shaanxi University of Science and Technology, Weiyang District, Xi'an 710021, China;Key Laboratory of Auxiliary Chemistry and Technology for Chemical Industry, Ministry of Education of China, Shaanxi University of Science and Technology, Weiyang District, Xi'an 710021, China |
| |
| Abstract: | |
| |
| Keywords: | Bi2Ti2O7 thin film self-assembled monolayer film dielectric properties |
|