| 化学浴沉积法制备高取向钒酸铋薄膜 |
| |
| 引用本文： | 刘晶冰,汪浩,张慧明,张文熊,严辉.化学浴沉积法制备高取向钒酸铋薄膜[J].无机化学学报,2007,23(7):1299-1302. |
| |
| 作者姓名： | 刘晶冰 汪浩 张慧明 张文熊 严辉 |
| |
| 作者单位： | 北京工业大学材料学院,北京,100022 |
| |
| 基金项目： | 国家自然科学基金;北京工业大学校科研和教改项目 |
| |
| 摘 要： | Highly oriented BiVO4 films were synthesized on glass substrates by modified chemical bath deposition (CBD). The influence of the deposition parameters as temperature and time of deposition on the rate of process and the quality of BiVO4 films was studied by XRD, Raman Spectroscopy and SEM. The film deposited at 90 ℃ for 12 h was dense and uniform. The BiVO4 thin film under this optimal depositing conditions was consisted of octagonal crystalline grains in a narrow size distribution with an average size of about 7 μm, showing a (004) preferential orientation.
|
| 关 键 词： | 钒酸铋(BiVO4)薄膜 化学浴沉积 择优取向 |
| 文章编号： | 1001-4861（2007）07-1299-04 |
| 修稿时间： | 2007-04-102007-05-30 |
Preparation of Oriented BiVO4 Thin Film by Chemical Bath Deposition |
| |
| LIU Jing-Bing,WANG Hao,ZHANG Hui-Ming,ZHANG Wen-Xiong and YAN Hui.Preparation of Oriented BiVO4 Thin Film by Chemical Bath Deposition[J].Chinese Journal of Inorganic Chemistry,2007,23(7):1299-1302. |
| |
| Authors: | LIU Jing-Bing WANG Hao ZHANG Hui-Ming ZHANG Wen-Xiong and YAN Hui |
| |
| Institution: | College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022,College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022,College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022,College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022 and College of Materials Science and Engineering, Beijing University of Technology, Beijing 100022 |
| |
| Abstract: | |
| |
| Keywords: | BiVO4 film chemical bath deposition orientation |