Thermal research of montmorillonite synthetized from the oxides SiO2-Al2O3-MgO-CaO |
| |
| Authors: | J. Masár Ľ. Kuchta H. Gerthofferová V. Š. Fajnor |
| |
| Affiliation: | (1) Department of Inorganic Chemistry, Faculty of Natural Sciences, Comenius University, Mlynská dolina, 842 15 Bratislava;(2) Geological Institute, Faculty of Natural Sciences, Comenius University, Zadunajská 15, 851 01 Bratislava, Czechoslovakia |
| |
| Abstract: | The thermal behaviour of synthetic montmorillonite of relatively simple chemical composition has been studied and interpreted. Montmorillonite was prepared by hydrothermal synthesis at 300° and 8.8 MPa during 165 hours. With the methods of DTA, DTG, TG, X-ray diffraction analysis, infrared spectroscopy and electron microscopy it was proved that the synthetic montmorillonite is a monomineral sample and no differences from natural montmorillonite were observed.
Zusammenfassung Das thermische Verhalten synthetischer Montmorillonite verhältnismässig einfacher chemischer Zusammensetzung wurde untersucht und gedeutet. Montmorillonit wurde durch hydrothermische Synthese bei 300°C und 8.8 MPa in 165 Stunden hergestellt. Durch die Methoden der DTA, DTG, TG, Röntgendiffraktionsanalyse, Infrarotspektroskopie und Elektronenmikroskopie wurde erwiesen, daß synthetische Montmorillonit eine monominerale Probe ist und keine Abweichungen von natürlichem Montmorillonit beobachtet werden konnten.
                          .   165 300° 8.8  .    ,  , ,   ,    , .
|
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|