薄钢片动态撕裂中断裂韧性的评定
引用本文:M.ABERKANE A.UIBRAHIM.薄钢片动态撕裂中断裂韧性的评定[J].宁波大学学报(理工版),2003,16(4):342-348.
作者姓名:M.ABERKANE  A.UIBRAHIM
作者单位:[1]DepartementdeGenieMecanique,FaculteduCeniedelaConstruction,UniversiteMouloudMammerideTizi-Ouzou,BP17RP,Tizi-Ouzou15000,Algeria [2]Laboratoired‘EnergetiqueMecaniqueetMateriaux,UniversitedeBoumerdes35000,Algeria;
摘    要:提出了一个关于薄钢片动态撕裂试验能量分析法.在摆锤冲击试验机上按原始的实验方法获得了起始动态断裂韧性R0,dyn,和动态撕裂模量Tdym,为了比较对同样材料进行了静态撕裂试验,以研究加载率V对断裂基本功ГC的影响.结果表明,在加载率1mm/min到300mm/min的变化范围内,断裂基本功Гc随加载率的对数略有下降.由于屈服应力随加载率而增加,作R0,dyn和Tdyn的比较时,观察到动态断裂韧性较之静态结果有一个明显的下降.

关 键 词:薄钢片  动态撕裂  韧性撕裂  裤形撕裂试验  断裂功  摆锤冲击试验机  断裂韧性

Fracture Toughness Evaluation in Dynamic Tearing of Thin Sheet Steel
M.ABERKANE,A.OUIBRAHIM.Fracture Toughness Evaluation in Dynamic Tearing of Thin Sheet Steel[J].Journal of Ningbo University(Natural Science and Engineering Edition),2003,16(4):342-348.
Authors:MABERKANE  AOUIBRAHIM
Abstract:This paper presents an energy analysis during dynamic tearing tests of thin steel sheet. These experiments are performed on a Charpy test device using an original experimental method. Dynamic fracture toughness at initiation R0,dyn and dynamic tearing modulus Tdyn are obtained. For a comparison purpose, static trousers tearing tests are conducted, on the same material, in order to study the influence loading rate V on the essential work of fracture Гe (calculated from Mai and Cotterell (1984) analysis). We have shown that by varying the loading rate from 1 mm/min to 300 mm/min, the essential work of fracture Гe decreases slowly with the Loga rithm of the loading rate V. A significant drop of dynamic fracture toughness compared to static one is observed,while making a comparison between R0,dyn and Гe (1 mm/rmin) due to the increase of yield stress with loading rate.
Keywords:ductile tearing  trousers test  work of fracture  Charpy test device  petalling