Direct patterning of poly(amic acid) and low‐temperature imidization using a crosslinker,a photoacid generator,and a thermobase generator

A positive‐type photosensitive polyimide (PSPI) based on poly(amic acid) (PAA), a crosslinker 1,1,1‐tris{4‐2‐(vinyloxy)ethoxy]phenyl}ethane (TVPE), a photoacid generator (PAG) (5‐propylsulfonyloxyimino‐5H‐thiophen‐2‐ylidene)‐2‐(methylphenyl)acetonitrile (PTMA), and a thermobase generator (TBG) t‐butyl 2,6‐dimethylpiperidine‐1‐carboxylate (BDPC) has been developed as a promising material in microelectronics. The PAA was prepared from 3,3′,4,4′‐biphenyltetracarboxylic dianhydride (BPDA) and 4,4′‐oxydianiline (ODA) in dimethyl sulfoxide (DMSO). The PSPI, consisting of PAA (69 wt %), TPVE (21 wt %), PTMA (3 wt %), and BDPC (7 wt %), showed high sensitivity of 21 mJ/cm² and a high contrast of 6.8 when it was exposed to a 436‐nm line (g‐line), postbaked at 90 °C for 5 min, and developed with 1.69 wt % TMAHaq. A clear positive image of 8 μm line and space pattern was printed on film, which was exposed to 50 mJ/cm² of g‐line by a contact printing mode and fully converted to the corresponding polyimide (PI) pattern on heating at 200 °C, confirmed by FTIR spectroscopy. Thus, this system will be a good candidate for next generation PSPIs. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3362–3369, 2009