Nonlinear optical polyimides consisting of chromophore‐containing dendrons with site‐isolation effect

To investigate the dendritic structure effects on the electro‐optical (EO) coefficients and thermal stability of the nonlinear optical (NLO) active materials, a bifunctional compound, IDD (4‐isocyanato‐4′(3,3‐dimethyl‐ 2,4‐dioxo‐acetidino)‐diphenylmethane) was used as a building block to synthesize a series of novel NLO chromophore‐containing dendritic structures including Generation 0.5 (G0.5) to Generation 3 (G3). The glass transition temperatures (T_g) of G1–G3 dendrons were in the range of 76–116°C, whereas only the G0.5 dendron exhibited a melting temperature (T_m), 98°C. Moreover, a series of NLO‐active guest–host systems ranging from polyimide‐G0.5 (PI‐G0.5) to polyimide‐G3 (PI‐G3) were prepared by blending 20 wt% chromophore‐containing dendron with a high T_g polyimide. EO coefficients ranged from 6.1 to 12.9 pm/V. The r₃₃/dye content ratio increased with increasing generation of dendron‐containing polyimide samples. Particularly, the improvement in r₃₃/dye content ratio of PI‐G2.5 sample tripled as compared to that of the guest–host sample with Disperse Red 1. Excellent temporal stability of PI‐G0.5 and PI‐G1.5 at 80°C was obtained. Moreover, waveguide properties for NLO polymers containing higher generation dendrons (3.1–3.6 dB/cm at 830 nm) were also obtained. Copyright © 2008 John Wiley & Sons, Ltd.