Electrical,structural, magnetic and transport properties of Zn2BaFe16O27 doped with Cu

Series of polycrystalline samples of Zn_2−xCu_xBaFe₁₆O₂₇ were prepared by usual ceramic methods, where x=0.0, 0.4, 0.6, 0.8, 1.0, 1.4. X-ray analysis done at room temperature using CoK_α with λ=1.790 Å confirms the presence of W-type hexaferrite phase structure. Saturation magnetization and hysteresis loops curves measurements at room temperature were studied as a function of Cu²⁺ substitution. It can be seen that the Cu²⁺ content slightly decreases the saturation magnetization from 25 to 20 emu g⁻¹; all hysteresis loops are closed, which indicates low anisotropy field and low saturation magnetization field. The dc conductivity and thermoelectric power were measured in a range from room temperature up to T=750 K for all samples. The thermoelectric power decreases on increasing Cu²⁺ content, and the conductivity increases with temperature. The value of the charge-carrier concentration increases by increasing the temperature and Cu²⁺ content.