The effect of magnetic field heat treatment on magnetostriction of Terfenol-D 2-2 composites

Based on the analysis of the magnetostriction for Terfenol-D composites, Terfenol-D 2-2 magnetostrictive composites have been prepared with laminations perpendicular to [1 1 2] axes. Then one of the samples was annealed in the vacuum at 423 K for 15 min at the magnetic field of 240 kA/m, which is along the direction of laminations and vertical to the [1 1 2] axes of the specimen. The static magnetostriction λ and dynamic magnetostrictive coefficient d₃₃ of samples were measured under the compressive stress of 0, 2, 4, 6 and 8 MPa. Effects of the compressive stress and the magnetic field heat treatment on the magnetostriction λ have been investigated. It is found that the magnetostriction of 2-2 composites can be improved under the compressive stress when the magnetic field is larger than 20 kA/m. The magnetostriction of 2-2 composites with the magnetic field heat treatment increases under compressive stress, and it can reach 1390×10⁻⁶ at the magnetic field of 200 kA/m and under the compressive stress of 4 MPa, much larger than the value of 860×10⁻⁶ without the magnetic field heat treatment. The highest magnetostriction of the 2-2 composite with the magnetic field heat treatment can reach 1530×10⁻⁶. The dynamic magnetostrictive coefficient d₃₃ of 2-2 composites with the magnetic field heat treatment have been improved, compared with that without magnetic field heat treatment. The maximum value of d₃₃ of the sample with magnetic field heat treatment is 71% larger than that without magnetic field heat treatment.