Atomic layer deposited HfO2 based metal insulator semiconductor GaN ultraviolet photodetectors

A report on GaN based metal insulator semiconductor (MIS) ultraviolet (UV) photodetectors (PDs) with atomic layer deposited (ALD) 5-nm-thick HfO₂ insulating layer is presented. Very low dark current of 2.24 × 10⁻¹¹ A and increased photo to dark current contrast ratio was achieved at 10 V. It was found that the dark current was drastically reduced by seven orders of magnitude at 10 V compared to samples without HfO₂ insulating layer. The observed decrease in dark current is attributed to the large barrier height which is due to introduction of HfO₂ insulating layer and the calculated barrier height was obtained as 0.95 eV. The peak responsivity of HfO₂ inserted device was 0.44 mA/W at bias voltage of 15 V.