十八碳键合钛胶固定相的制备及其色谱性能

 以聚合诱导胶体凝聚法 (PICA)合成的窄粒径分布的TiO2 多孔微球 (表面积 :3 6 7m2 /g ,孔容 :0 3 0mL/g ,平均孔径 :3 2 2nm ,平均粒径 :3 5 μm)为基质 ,与十八碳三甲氧基硅烷的甲苯溶液共同回流 8h ,制得十八碳键合钛胶固定相 (ODT)。该固定相的含碳量为 2 87% (即 0 66μmol/m2 ) ,疏水选择性为 0 4 63 8。将其用于分离中性和碱性化合物时 ,显示出比较好的色谱性能。

Preparation and Chromatographic Characteristics of Octadecyl Bonded Titania Sta tionary Phase for High Performance Liquid Chromatography

Porous titania microspheres (surface area: 36.7 m2/g, average pore volume: 0.30 mL/g, average pore diameter: 32.2 nm, average diameter: 3.5 microns) with a very narrow particle size distribution, were synthesized by refluxing polymerized-induced colloid aggregation (PICA), with octadecyltrimethoxysilane in toluene as a solvent for 8 h, and octadecyltitania stationary phase (ODT) was obtained. The carbon content and hydrophobic selectivity of the stationary phase were 2.87% (i.e. 0.66 mumol/m2) and 0.4638, respectively. ODT showed good chromatographic performances when it was used to separate the neutral and basic solutes using methanol solution as a mobile phase.