Abstract: | A superconducting oxide with a stoichiometry La3CaBa3Cu7O15.5+x, in which x = 0.75, was prepared. It had a tetragonal triple-perovskite structure with lattice parameters a = 3.879 Å and c = 11.637 Å. According to resistivity measurements, a sharp superconducting transition, ΔTc(10-90%) = 1.5 K, and Tc(zero) = 80 K were observed. When it was measured at a small magnetic field (10-20 gauss) with field cooling, the sintered pellet showed a positive magnetic susceptibility, but the powdered sample exhibited (he diamagnetism of a typical superconductor. However, no peculiar shielding effect was found in both the sintered and powdered samples. |