Dynamic study of the noncrystalline phase of 13C-labeled polyethylene by variable-temperature 13C CP/MAS NMR spectroscopy

The ¹³C spin-lattice relaxation times T₁ of ¹³C-labeled polyethylene crystallized under different conditions were measured at temperatures from ?120 to 44°C by variable-temperature solid-state high-resolution ¹³C nuclear magnetic resonance (NMR) spectroscopy, in order to determine accurately the dynamics of the noncrystalline region of the polymer. From these results, it was found that the T₁ minimum for the CH₂ carbons in the noncrystalline region of solution-crystallized polyethylene with high crystallinity appears at higher temperature by about 20°C than that of melt-quenched polyethylene with low crystallinity. This means that the molecular motion of the CH₂ carbons in the noncrystalline regions is more constrained at a given temperature in the material of higher crystallinity. Furthermore, dynamics of the noncrystalline region is discussed in terms of the ¹³C dipolar dephasing times.