Electrical and photocatalytic properties of Na2Ti6O13 nanobelts prepared by molten salt synthesis

Single-crystalline Na₂Ti₆O₁₃ nanobelts were prepared on large-scale by molten salt synthesis at 825 °C for 3 h. The obtained nanobelts have typical width of less than 200 nm and thickness of 10-30 nm, and length up to 10 μm. The growth direction of the nanobelts was determined to be along [0 1 0]. Electrical transport property of an individual nanobelt was measured at room temperature and ambient atmosphere, and results showed that the nanobelts are semiconductor. Na₂Ti₆O₁₃ nanobelts exhibited good photocatalytic efficiency for the degradation of RhB under UV irradiation.