Double layer oxidation resistant coating for carbon fiber reinforced silicon carbide matrix composites

Double layer coatings, with celsian-Y₂SiO₅ as inner layer and Y₂Si₂O₇ as outer layer, were prepared by microwave sintering on the surface of carbon fiber reinforced silicon carbide matrix composite. Both celsian, Y₂SiO₅ and Y₂Si₂O₇ were synthesized by in situ method using BAS glass, Y₂O₃ and SiO₂ as staring materials. The sintering temperature was 1500 °C, and little damage was induced to the composite. The composition and micrograph of the fired coating were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The oxidation and thermal shock resistance of samples with doubled-layered coating were characterized at 1400 °C in air. After 150 min oxidation and thermal cycling between 1400 °C and room temperature for 15 times, the weight loss of double layer-coated sample was 1.22% and there were no cracks in the coating.