Effect of dislocation loops in macroscopically dislocation-free GaP substrates on the perfection of homo-epitactic deposits

Substrates and epitactic layers of GaP are etched under optimized conditions with the defect-revealing, preferential R-C etchant and subsequently examined using high-magnification (about 2500X) optical microscopy techniques. It is possible then to distinguish two new phenomena, viz. etch pits characteristic of dislocation loops in the substrate, and inclined dislocation dipoles in the layer. For layers grown on dislocation-free substrates we find that (i) the surface densities of both defects are equal (～5 × 10⁵cm^-2), and (ii) the average diameter of the dislocation loops in the substrate is roughly the same as the average distance between the two dislocations of the dislocation dipoles (0.5?1μm). Hence the perfection of these layers is determined by interfacial dislocation loops. Because the density of dislocation loops is only about a factor of two lower in highly (～1 × 10⁵ cm^-2) dislocated substrates, growth on these substrates results in layers which have even slightly lower dislocation density than layers grown on dislocation-free substrates. In the former case also single dislocations in the substrate propagate into the layer. Minority-carrier lifetime data indicate that minority-carrier recombination at dislocations is a restrictive factor for the luminescence quality of layers grown both on dislocation-free and highly-dislocated substrates.