High-pressure neutron diffraction study ofBaFe2As2 |
| |
| Authors: | J.-E.?J?rgensen T. C.?Hansen |
| |
| Affiliation: | 1.University of Aarhus,Aarhus C,Denmark;2.Institute Max von Laue-Paul Langevin,Grenoble Cedex 9,France |
| |
| Abstract: | The crystal structure of BaFe2As2 was studied by high-pressure neutron powder diffraction in the pressure range from ambient to 6.5 GPa as well as in the temperature range from 12 K to 293 K at 4.4 GPa and no pressure or temperature induced phase changes were observed. The compression mechanism of BaFe2As2 was found to be anisotropic as the a- and c-axes are reduced by 2.49 and 3.66%, respectively at 6.5 GPa. Within the FeAs layers the Fe-As and Fe-Fe bonds decrease by 2.49 and 3.66%, respectively. The Ba-As distance decreases by 3.70% while the As-As inter-atomic distance along the c-axis exhibits a complex pressure dependence. The bulk modulus B 0 and its pressure derivative B 0' were determined to be B 0 = 59(2) GPa and B 0' = 6.1(7) at ambient temperature. |
| |