Comparative study of the kinetics of non-isothermal melt solidification of random copolymers of butene-1 with either ethylene or propylene

The kinetics of non-isothermal melt solidification of random butene-1/propylene copolymers has been compared with that of random butene-1/ethylene copolymers. Analysis of the distance between neighbored chain segments in the crystal phase revealed inclusion of propylene chain defects into crystals, while ethylene co-units are excluded from crystallization. As a consequence of different acceptance of propylene and ethylene chain defects to participate in crystallization, the kinetics of the transition of the melt into ordered phase is significantly slower in random butene-1/ethylene copolymers. For samples of similar co-unit concentration, the decrease of the crystallization temperature and of the critical cooling rate to suppress ordering/crystallization is higher in random butene-1/ethylene copolymers than in butene-1/propylene copolymers. Due to the required rejection of ethylene co-units at the crystal growth front, ultimately, the maximum crystallinity is lower in butene-1/ethylene copolymers than in butene-1/propylene copolymers of similar amount of co-units.