Correlation between local mobility and mechanical properties of high‐speed melt‐spun nylon‐6 fibers

This article establishes the processing–microstructure–motion–property relationship of high‐speed melt‐spun nylon‐6 fibers. From solid‐state ¹H NMR T_1ρ (spin–lattice relaxation time in the rotating frame) relaxation studies, all nylon‐6 fibers spun at 4500–6100 m/min showed three‐component exponential decay with the time constants T_1ρ,I, T_1ρ,II, and T_1ρ,III, indicating that there existed three different motional phases. These phases were assigned to immobile crystalline, intermediate rigid amorphous, and mobile amorphous regions. The determination of the correlation time (τ_c) of the respective phases provided information about the local molecular mobility of each phase with respect to the spinning speed. As the spinning speed increased, τ_c of the crystalline region increased (4500–5200 m/min) and then reached a plateau. However, τ_c for the rigid amorphous region increased from 5200 m/min onward, indicating that the rigid amorphous chains were more oriented and constrained in the spinning speed range of 5500–6100 m/min. The drastic increase of the maximum thermal stress for all fibers from 5500 to 6100 m/min was coincident with the τ_c characteristics of the rigid amorphous region. The significant increase in tenacity and Young's modulus and the large decrease in elongation at break at 5500–6100 m/min were also in good agreement with the local molecular motion of the intermediate rigid amorphous phase in the nylon‐6 fibers. © 2001 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 39: 993–1000, 2001