Catalytic Performance and Characterization of Pt‐Co/Al2O3 Catalysts for CO2 Reforming of CH4 to Synthesis Gas

Pt‐Co/Al₂O₂ catalyst has been studied for CO₂ reforming of CH₄ to synthesis gas. It was found that the catalytic performance of me catalyst was sensitive to calcination temperature. When Co/Al₂O₃ was calcined at 1473 K prior to adding a small amount of Pt to it, the resulting bimetallic catalyst showed high activity, optimal stability and excellent resistance to carbon deposition, which was more effective to the reaction than Co/Al₂O₃ and Pt/Al₂O₃ catalysts. At lower metal loading, catalyst activity decreased in the following order: Pt‐Co/ Al₂O₃ > Pt/Al₂O₃ > Co/Al₂O₃. With 9% Co, the Co/Al₂O₃ calcined at 923 K was also active for CO₂ reforming of CH₄, however, its carbon formation was much more fast man that of the Pt‐Co/Al₂O₃ catalyst. The XRD results indicated that Pt species well dispersed over the bimetallic catalyst. Its high dispersion was related to the presence of CoAl₂O₄, formed during calcining of Co/Al₂O₃ at high temperature before Pt addition. Promoted by Pt, Co/Al₂O₄ in the catalyst could be reduced partially even at 923 K, the temperature of pre‐reduction for the reaction, confirmed by TPR. Based on these results, it was considered that the zerovalent platinum with high dispersion over the catalyst surface and the zerovalent cobalt resulting from Co/Al₂O₄ reduction are responsible for high activity of the Pt‐Co/Al₂O₃ catalyst, and the remain Co/Al₂O₄ is beneficial to suppression of carbon deposition over the catalyst.