Magnetic entropy-change in La0.67−xBixCa0.33MnO3 compound

Bi doped lanthanum manganites with the chemical composition of La_0.67−xBi_xCa_0.33MnO₃ (x=0$x=0$, 0.05, 0.1, 0.2) were prepared by the standard solid-state process. The Curie temperatures were measured to be 267 K for x=0$x=0$, 248 K for x=0.05$x=0.05$, 244 K for x=0.1$x=0.1$ and 229 K for x=0.2$x=0.2$ samples. It was found that the maximum value of the magnetic entropy change ∣ΔS_m∣ has reached the highest value of 6.08 J/kg K at 3 T for the composition with x=0.05$x=0.05$. Nearly the same maximum entropy change was observed for the x=0$x=0$ sample. A large decrease in the magnitude of the entropy change was observed for the x=0.2$x=0.2$ sample.