Exchange coupling and remanence enhancement in nanocomposite Nd–Fe–B/FeCo multilayer films

Nd–Fe–B-type hard phase single layer films and nanocomposite Nd₂₈Fe₆₆B₆/Fe₅₀Co₅₀ multilayer films with Mo underlayers and overlayers have been fabricated on Si substrates by rf sputtering. The hysteresis loops of all films indicated simple single loops for fixed Nd–Fe–B layer thickness (10 nm) and different FeCo layer thickness (d_FeCo=1–50 nm). The remanence of these films is found to increase with increasing d_FeCo and the coercivity decrease with increasing d_FeCo. It is shown that high remanence is achieved in the nanocomposite multilayer films consisting of the hard magnetic Nd–Fe–B-type phase and soft magnetic phase FeCo with 20 nm?d_FeCo?3 nm. The sample of maximum energy product is 27 MG Oe for d_FeCo=5 nm at room temperature. The enhancement of the remanence and energy products in nanocomposite multilayer films is attributed to the exchange coupling between the magnetically soft and hard phases.