Influence of pH on characteristics of BaFe12O19 powder prepared by sol–gel auto-combustion

BaFe₁₂O₁₉ powders with nanocrystalline sizes were produced by sol–gel auto-combustion. Fe³⁺ and Ba²⁺, in a molar ratio of 11.5, were chelated by citric acid ions at different pH. After dehydration, auto-combustion and calcinations, BaFe₁₂O₁₉ powders were formed. TG/DSC indicated the action to form BaFe₁₂O₁₉ first occurred at about 800. XRD patterns of the annealed powders showed that the well-crystalline powder was produced when pH=10. In addition, the data from XRD showed the lattice parameters a and c, and the unit-cell volume V had a little decrease and the density went up with the increasing pH. The data from PPMS exhibited that pH in the starting solution had an important influence on magnetic properties. In this case, BaFe₁₂O₁₉ powder, of maximum magnetization M(3 T)≈60 A m²/kg, the remanent magnetization M_r≈33 A m²/kg and the intrinsic coercive H_c≈432 kA/m, was produced under the molar ratio of citric acid to the metal nitrate of 1.5 when pH=10.