Effect of La doping on magnetotransport and magnetic properties of double perovskite Sr2FeMoO6 system

We have investigated the magnetotransport and magnetic properties on polycrystalline samples of Sr_2−xLa_xFeMoO₆ (x=0$x=0$, 0.2, 0.4, 0.6, 0.8 and 1.0). The magnitude of intergrain tunneling magnetoresistance with low magnetic field of 0.88 T for x=0.2$x=0.2$ and 0.4$0.4$ samples are as large as 5% and 7% at room temperature and 13% and 10% at 10 K, respectively. The increase of coercivity (_Hc$H_{\mathrm{c}}$), ratio of remanent magnetization with respect to saturation magnetization (_Mr/_Ms$M_{\mathrm{r}}/M_{\mathrm{s}}$), high saturation fields, and reduction of the saturation magnetization indicate that random disorder of spin orientation is mainly responsible for enhancement of the low-field magnetoresistance for samples with x?0.4$x?0.4$. Whereas rapid drop of _Hc$H_{\mathrm{c}}$, _Mr/_Ms$M_{\mathrm{r}}/M_{\mathrm{s}}$, _Mr$M_{\mathrm{r}}$, and saturation fields for samples with x>0.4$x>0.4$ signifies the growth of antiphase boundary, which gives rise to lower values of low-field MR.