Infrared emissions, visible up-conversion, thermoluminescence and defect centres in Er3Al5O12 phosphor obtained by solution combustion reaction

The Er₃Al₅O₁₂ phosphor powders were prepared using the solution combustion method. Formation and homogeneity of the Er₃Al₅O₁₂ phosphor powders have been verified by X-ray diffraction and energy-dispersive X-ray analysis respectively. The frequency up-conversion from Er₃Al₅O₁₂ phosphor powder corresponding to the ²H_9/2 → ⁴I_15/2, ²H_11/2 → ⁴I_15/2, ⁴S_3/2 → ⁴I_15/2, ⁴F_9/2 → ⁴I_15/2 and the infrared emission (IR) due to the ⁴I_13/2 → ⁴I_15/2 transitions lying at ∼410, ∼524, ∼556, 645–680 nm and at ∼1.53 μm respectively upon excitation with a Ti-Sapphire pulsed/CW laser have been reported. The mechanism responsible for the frequency up-conversion and IR emission is discussed in detail. Defect centres induced by radiation were studied using the techniques of thermoluminescence and electron spin resonance. A single glow peak at 430°C is observed and the thermoluminescence results show the presence of a defect center which decays at high temperature. Electron spin resonance studies indicate a center characterized by a g-factor equal to 2.0056 and it is observed that this center is not related to the thermoluminescence peak. A negligibly small concentration of cation and anion vacancies appears to be present in the phosphor in accordance with the earlier theoretical predictions.