Mixed-mode failure of composite laminates with cracks

The behavior of quasi-isotropic graphite/epoxy laminates with cracks subjected to various biaxial-stress fields was studied experimentally. This was accomplished by uniaxial tensile loading of specimens with cracks of various orientations with the loading axis. It was found that the critical stress-intensity factor, based on a projected crack length increased by a characteristic damage dimension, is nearly constant with stress biaxiality and initial crack length. Paper was presented at V International Congress on Experimental Mechanics held in Montreal, Quebec, Canada on June 10–15, 1984.