Crystalline-structure-dependent green and red upconversion emissions of Er-Yb-Li codoped TiO2

Crystalline structures and infrared-to-visible upconversion luminescence spectra have been investigated in 1 mol% Er³⁺, 10 mol% Yb³⁺ and 0-20 mol% Li⁺ codoped TiO₂ 1Er10Yb(0-20)Li:TiO₂] nanocrystals. The crystalline structures of 1Er10Yb(0-20)Li:TiO₂ were divided into three parts by the addition of Yb³⁺ and Li⁺. Both green and red upconversion emissions were observed from the ²H_11/2/⁴S_3/2 → ⁴I_15/2 and ⁴F_9/2 → ⁴I_15/2 transitions of Er³⁺ in Er³⁺-Yb³⁺-Li⁺ codoped TiO₂, respectively. The green and red upconversion emissions of 1Er:TiO₂ were enhanced significantly by Yb³⁺ and Li⁺ codoping, in which the intensities of green and red emissions and the intensity ratio of green to red emissions (I_green/I_red) were highly dependent on the crystalline structures. The significant enhanced upconversion emissions resulted from the energy migration between Er³⁺ and Yb³⁺ as well as the distortion of crystal field symmetry of Er³⁺ caused by the dissolving of Li⁺ at lower Li⁺ codoping concentration and the phase transformation at higher Li⁺ concentration. It is concluded that codoping with ions of smaller ionic radius like Li⁺ can efficiently improve the upconversion emissions of Er³⁺ or other rare-earth ions doped luminsecence materials.