Isospecific polymerizations of alkyl methacrylates with a bis(alkyl)Yb complex and formation of stereocomplexes with syndiotactic poly(alkyl methacrylate)s

Yb[C(SiMe₃)₃]₂ initiates the living polymerization of methyl methacrylate (MMA) at −78°C to give the polymer with M_n of 51.0×10⁴ (M_w/M_n=1.1) and high isotacticity (97%) in a quantitative yield. Mixing of the acetone solution of resulting polymer (M_n=16.3×10⁴) with the acetone solution of syndiotactic poly(MMA) (M_n=15.7×10⁴) prepared by the (C₅Me₅)₂SmMe(THF) initiator produces desired stereocomplex in high yield bearing very high T_m whose tensile modulus is higher than the respective isotactic and syndiotactic poly(MMA)s. Yb[C(SiMe₃)₃]₂ also generated isotactic (98%) poly[2-(dimethylamino)ethyl methacrylate] (DMEMA), and (C₅Me₅)₂SmMe(THF) affords the syndiotactic (97%) polymer in high yields. The combination of isotactic poly(MMA)-block-poly(DMEMA) (97/3) and syndiotactic poly(MMA)-block-poly(DMEMA) (97/3) provides the amphiphathic stereocomplex. In sharp contrast to the catalysis of Yb[C(SiMe₃)₃]₂ in toluene, the addition of THF or HMPA resulted in the formation of syndio-rich poly(MMA).