Neutron powder diffraction on RbCrl3 and magnetic measurements on RbCrl3 and CsCrl3

β-RbCrI₃ (a = 13.772(3), b = 8.000(2), c = 7.069(2) Å β = 95.85(1)°, $\text{Z = 4,}\text{C2}\text{m}$ at 293 K) and γ-RbCrI₃ (a = 13.586(2), b = 7.923(2), c = 14.094(3) Å, β = 96.88(1)°, Z = 8, C2 at 1.2 K) are isostructural to β-RbCrCl₃ and γ-RbCrCl₃ and are both Jahn-Teller distorted BaNiO₃ structures. In both compounds elongated octahedra occur. γ-RbCrI₃ most probably has a magnetic spiral structure at 4.2 and 1.2 K. Theoretically, a spiral propagating along the b axis is expected. A model with k = 9/19b1 yielded the best result. However, no good fit was obtained possibly because of a misfit in k and canting of the magnetic moments due to anisotropy. χ vs T single-crystal measurements on β-CsCrI₃ are in accordance with its magnetic structure. The three-dimensional magnetic ordering temperature T_c is estimated as 27(1) K. From the χ vs T curves of γ-RbCrI₃, T_c could not be determined. From fits to χ vs T powder data $\text{J}\text{k}$ of CsCrI₃ and RbCrI₃ are estimated to be ?14(2) and ?11(1) K, respectively.