Poly(pentamethylcyclopentasiloxane). I. Synthesis and characterization

We have discovered that pentamethylcyclopentasiloxane (D₅H) can be readily polymerized into poly(pentmethylcyclopentasiloxane) (PD₅) with a Pt (Karstedt) catalyst in the presence of water in bulk or in solution at 100 °C and that the product is a solid with extraordinary properties. The polymerization starts with the oxidation of the SiH groups by water into an intermediate containing SiOH groups (SiH + H₂O → SiOH + H₂), which is followed immediately by the condensation (2SiO → Si? O? Si) of D₅H rings into complex aggregates of cyclosiloxane moieties. According to Raman spectroscopy, an average of three of the five SiH functionalities are converted, and the final product contains only a negligible number of SiOH groups. The melting and glass‐transition temperatures of the monomer are exceptionally low: T_m,D5H = ?137.6 ± 1 and T_g,D5H = ?152 ± 2 °C. The polymer exhibits an unprecedented combination of properties: it is a stiff and brittle solid, is insoluble in common solvents, does not exhibit a melting endotherm but has an extremely low glass transition (T_g,PD5 = ?151 ± 0.5 °C), and is thermally stable up to at least 700 °C. Brillouin scattering indicates very slow variation of the relaxation time with temperature, a property characteristic of strong glass‐forming systems such as silica glass. This characteristic may account for the unique combination of properties of the new polymer: an extremely low glass‐transition temperature combined with solidlike properties even at ambient temperature (more than twice its glass‐transition temperature). © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1285–1292, 2002