The effect of light on the viscosity and molecular mass of nitrocellulose

The photodegradation of a series of nitrocellulose (NC) samples with nitrogen contents ranging from 11.69% to 13.55% has been investigated by observing changes in molecular mass and viscosity using, respectively, size exclusion chromatography (SEC) and a modified cone and plate rheometer. When NC in γ-butyrolactone was subjected to UV light in the range 320-390 nm its specific viscosity (η_sp) was found to decrease noticeably, a change attributed to polymer chain scission and de-aggregation. This view was supported by an observed reduction in the mass average molecular mass (M_w). In contrast, irradiation with a single wavelength at 365 nm did not significantly change either η_sp or M_w and similar behaviour was observed when NC solutions were irradiated with visible light (400-500 nm). In the solid state, the photodegradation of water-wet NC is faster than that of the dried material, which is attributed to the catalytic effect of acids formed from the reaction between water and nitrogen oxides (NO_x) arising from NC decomposition. A higher degree of crystallinity in the NC, as found by X-ray diffraction (XRD), was shown to lead to a smaller decrease in viscosity and molecular mass. This is thought to be because the photodegradation reaction is suppressed in crystalline NC by more effective radical-radical recombination.