Composition dependence of the structural chemistry and magnetism of Ca2.5Sr0.5(Ga,Co)1+xMn2−xO8

Polycrystalline samples of bilayered brownmillerite-like Ca_2.5Sr_0.5GaCo_0.15Mn_1.85O₈ and Ca_2.5Sr_0.5Ga_1.2Mn_1.8O₈ have been prepared and characterised by magnetometry and neutron diffraction over a wide temperature range. The structural chemistry and magnetic properties are compared to those of Ca_2.5Sr_0.5GaMn₂O₈. Ga enrichment has a significant effect on the former but not on the latter, whereas changes in both occur when paramagnetic Co³⁺ cations enter the parent phase on the 4-coordinate sites. The coupling between the environment around the 4-coordinate cations and the transition to an antiferromagnetic ordered state that was observed in Ca_2.5Sr_0.5GaMn₂O₈ is not apparent in the cation-substituted compositions, although both show long-range antiferromagnetic order at low temperatures.