Structure and magnetism of NaRu2O4 and Na2.7Ru4O9 |
| |
Authors: | K.A. Regan Q. Huang A.P. Ramirez |
| |
Affiliation: | a Department of Chemistry, Princeton University, Princeton, NJ 08544, USA b NIST Center for Neutron Research, National Institute of Standards and Technology, Gaithersburg, MD 20899, USA c Department of Physics, Princeton University, Princeton, NJ 08544, USA d Bell Laboratories, Lucent Technologies, Murray Hill, NJ 07974, USA |
| |
Abstract: | The structures of NaRu2O4 and Na2.7Ru4O9 are refined using neutron diffraction. NaRu2O4 is a stoichiometric compound consisting of double chains of edge sharing RuO6 octahedra. Na2.7Ru4O9 is a non-stoichiometric compound with partial occupancy of the Na sublattice. The structure is a mixture of single, double and triple chains of edge-shared RuO6 octahedra. NaRu2O4 displays temperature independent paramagnetism with . Na2.7Ru4O9 is paramagnetic, χ0= with and a Curie constant of 0.0119 emu/mol Oe K. Specific heat measurements reveal a small upturn at low temperatures, similar to the upturn observed in La4Ru6O19. The electronic contribution to the specific heat (γ) for Na2.7Ru4O9 was determined to be15 mJ/moleRu K2. |
| |
Keywords: | Ruthenate Bronze NaRu2O4 Na2.7Ru4O9 Ferrite Paramagnetic |
本文献已被 ScienceDirect 等数据库收录! |
|