Effect of annealing temperature on the optical and electrical properties of amorphous As45.2Te46.6In8.2 thin films

The optical absorption of the As-prepared and annealed As_45.2Te_46.6In_8.2 thin films are studied. Films annealed at temperatures higher than 453 K show a decrease in the optical energy gap (E_o). The value of E_o increases from 1.9 to 2.43 eV with increasing thickness of the As-prepared films from 60 to 140 nm. The effect of thickness on high frequency dielectric constant (?_∞) and carrier concentration (N) is also studied. The crystalline structures of the As_45.2Te_46.6In_8.2 thin films resulting from heat treatment of the As-prepared film at different elevated temperatures is studied by X-ray diffraction. An amorphous-crystalline transformation is observed after annealing at temperatures higher than 453 K. The electrical conductivity at low temperatures is found due to the electrons transport by hopping among the localized states near the Fermi level. With annealing the films at temperatures higher than 473 K (the crystallization onset temperature) for 1 h, the electrical conductivity increases and the activation energy decreases, which can be attributed to the amorphous-crystalline transformations.