Summary A series of monodisperse polystyrene latices was prepared by using the direct and the seeding emulsion polymerization methods. The recipes for their preparation are given in full detail. Best results were obtained when using Aerosol MA (a surfactant of the sulfosuccinate series) as the emulsifier. The particle size distributions were evaluated from electron microscopic data. The average size of latex particles ranged from 200 to 950 m. The polydispersity ratios being very near unity and modal frequencies about 95% indicate a very high monodispersity of latex preparations. The reproducibility of the particle size distribution parameters was remarkably good. Significant deviation from theSmith-Ewart mechanism was found. A possible mechanism of the emulsifier action in the formation of monodisperse latices is postulated.

---

Zusammenfassung Es wurde eine Serie von monodispersen Polystyrollatices dargestellt. Die experimentellen Bedingungen, unter welchen monodisperse Latices entstehen, wurden untersucht. Die Vorschriften sind genau angegeben. Mit Aerosol MA (einem oberflächenaktiven Mittel der Sulfosuccinatserie) als Emulgator wurden die besten Ergebnisse erhalten. Mittels Elektronenmikroskopie wurde die Verteilung der Teilchengrößen ermittelt. Die durchschnittliche Größe der Latexteilchen lag zwischen 200 und 950 m. Die Polydispersitätsquotienten lagen in unmittelbarer Nähe von 1, und die modalen Frequenzen um 95% indizierten eine sehr hohe Monodispersität der Latexproben. Die Reproduzibilität der Teilchengröße-Verteilung-Parameter war besonders ausgeprägt. Es wurde eine Abweichung vomSmith-Ewart-Mechanismus beobachtet. Der mögliche Mechanismus der Emulgatorwirkung bei Entstehung der monodispersen Latices wurde diskutiert.

---

---

With 7 figures and 8 tables