Role of Al2O3 in upconversion and NIR emission in Tm and Er codoped calcium fluoro phosphorous silicate glass system

In this study, the principal role of Al₂O₃ on the features of the photoluminescence spectra of Tm³⁺ ion and upconversion phenomenon in Tm³⁺ and Er³⁺ codoped CaF₂−Al₂O₃−P₂O₅−SiO₂ glass system has been investigated. The concentration of Al₂O₃ is varied from 2 to 10 mol% while that of Er³⁺ and Tm³⁺ is fixed. IR and Raman spectral studies have indicated that there is a gradual increase in the degree of disorder in the glass network with increase in the concentration of Al₂O₃ up to 6.0 mol%. This is attributed to the presence of Al³⁺ ions in octahedral positions in larger proportions. When the glasses are doped with Tm³⁺ ions, the blue and red emissions were observed, whereas in Er³⁺ doped glasses blue, green and red emissions were observed. When the glasses are codoped with Tm³⁺ and Er³⁺ ions and excited at 790 nm, all the three emission lines were observed to be reinforced, especially in the glasses mixed with 6.0 mol% of Al₂O₃. The IR emission band detected at about 1.8 μm due to ³F₄→³H₆ transition of Tm³⁺ ions is also observed to be strengthened due to codoping. The reasons for enhancement in the intensity of various emission bands due to codoping have been identified and discussed with the help of rate equations for various emission transitions.