Optical properties of Mn-activated Na2SnF6 and Cs2SnF6 red phosphors

Alkaline hexafluorostantanate red phosphors Na₂SnF₆:Mn⁴⁺ and Cs₂SnF₆:Mn⁴⁺ are synthesized by chemical reaction in HF/NaMnO₄ (CsMnO₄)/H₂O₂/H₂O mixed solutions immersed with tin metal. X-ray diffraction patterns suggest that the synthesized phosphors have a tetragonal symmetry with the space group D_4h¹⁴ (Na₂SnF₆:Mn⁴⁺) and a trigonal symmetry with the space group D_3d³ (Cs₂SnF₆:Mn⁴⁺). Photoluminescence (PL) analysis, PL excitation (PLE) spectroscopy, and the Raman scattering techniques are used to investigate the optical properties of the phosphors. The Franck-Condon analysis of the PLE data yields the Mn⁴⁺-related optical transitions to occur at ∼2.39 and ∼2.38 eV (⁴A_2g→⁴T_2g) and at ∼2.83 and ∼2.76 eV (⁴A_2g→⁴T_1g) for Na₂SnF₆:Mn⁴⁺ and Cs₂SnF₆:Mn⁴⁺, respectively. The crystal field parameters (Dq) of the Mn⁴⁺ ions in the Na₂SnF₆ and Cs₂SnF₆ hosts are determined to be ∼1930 and ∼1920 cm⁻¹, respectively. Temperature-dependent PL measurements are performed from 20 to 440 K in steps of 10 K, and the obtained results are interpreted by taking into account the Bose-Einstein occupation factor. Comprehensive discussion is given on the phosphorescent properties of a family of Mn⁴⁺-activated alkaline hexafluoride salts.