| Abstract: | Polymers with both pendant spiro ortho ester and carboxylic acid moieties were synthesized by partial esterification of poly(methacrylic acid), poly(methacrylic acid-co-methyl methacrylate), or poly(methacrylic acid-co-styrene) with halomethylated spiro ortho esters in the presence of 1,8-diazabicyclo5,4,0]undecene-7 in dimethyl sulfoxide. The extent of esterification increased with increasing reaction temperature. The reaction of polymeric carboxylic acids with chloromethylated spiro ortho esters proceeded to 80% of conversion at 100°C for 120 h. In contrast, the degree of esterification with bromomethylated spiro ortho ester reached 80% at 60°C within 24 h. Thermo-crosslinking of polymers having pendant spiro ortho ester moiety and carboxylic acid could be effected in films. The rate of spiro ortho ester ring-opening increased with increasing reaction temperature and with increasing content of carboxylic acid groups in the polymer. Further, the rates of gel production were also measured. The polymer containing an equimolar mixture of spiro ortho ester moieties and carboxylic acids exhibited the highest reactivity. In addition, it was found that thermal crosslinking reaction of the polymer occurred with minimum volume shrinkage. |